How to control inter-diffusion between coatings and substrates at high temperatures?

    [abstract]  The inter-diffusion between coatings and substrates at high temperatures significantly influences the mechanical properties of alloys, especially for TiAl intermetallics and nickel base single crystals. The very important subject is to control inter-diffusion between them. We tested Ta, TiN, Cr2O3 and YSZ as diffusion barriers for TiAl and YSZ and NiCrO as diffusion barrier for N5 single crystals. The result indicated that Cr2O3, YSZ and NiCrO were good diffusion barriers, because of the formation of very stable Al2O3 layers during high temperature treatment, which significantly retarded the inter-diffusion between the coatings and substrates.

    時間：2016年8月10日11:30-12:00

    報告人：王福會

    個人簡介

王福會教授

    中國科學院金屬研究所研究員， 原中國科學院金屬腐蝕與防護研究所副所長。現(xiàn)任中國科學院金屬研究所二級研究員、博士生導師，96年度國家杰出青年基金獲得者。兼任中國腐蝕與防護學會第九屆理事長、中國腐蝕與防護學會第二屆青年工作委員會主任、中國腐蝕與防護學高溫專業(yè)委員會主任、中國機械工程學會表面工程分會副主任委員、《腐蝕科學與防護技術(shù)》主編，《中國腐蝕與防護學報》、《中國有色金屬學報》和《中國表面工程》編委以及多個國際雜志編委。

    主要從事高溫腐蝕與表面工程研究。首次提出高溫合金通過納米化實現(xiàn)自防護的概念，并成功地發(fā)展了具有我國自主知識產(chǎn)權(quán)的新一代高溫防護納米涂層，多次被邀做國際會議特邀報告。“抗高溫氧化和熱腐蝕的納米晶涂層”被評價為“是解決傳統(tǒng)涂層老問題的創(chuàng)新方法，可能會成為高溫涂層領(lǐng)域的新的研究方向”。他還開辟了固態(tài)鹽和水蒸氣綜合作用對材料中溫腐蝕的影響研究的新方向，揭示一些與傳統(tǒng)相悖的新現(xiàn)象，特別是在鹽和水蒸氣綜合作用下，隨Cr含量增加Fe-Cr合金的耐蝕性反而惡化，并提出了“動態(tài)水膜理論”揭示這一腐蝕規(guī)律。他發(fā)展的梯度TiAlN涂層、CoNiCrAlYHfSi涂層和金屬復合搪瓷涂層等成功應用于國防重大型號工程上。他1992年獲中國科學院院長獎學金特別獎、1993年獲國際材料聯(lián)合會頒發(fā)的青年科學家與工程師獎、1994年獲中國科學院有突出貢獻的中青年專家稱號、1995年獲中國科學院首屆優(yōu)秀青年稱號、1996年獲國務院政府特殊津貼、2001年獲中國科學院青年科學家獎、2005年獲中國優(yōu)秀博士后稱號、2010年 獲“遼寧省自然科學一等獎”（排名1）。工作期間獲得的項目資助包括：863項目5項、973一級課題3項、國防課題6項、國家自然科學基金6項以及國家杰出青年基金。發(fā)表SCI收錄論文250余篇，被他人引用1000多次，獲得發(fā)明專利30多項。到目前為止，共培養(yǎng)畢業(yè)博士研究生60多名，出站博士后10余名。