鋁合金腐蝕的標(biāo)準(zhǔn)匯總（列表）

2025-05-23 16:11:47 作者：本網(wǎng)整理來源：網(wǎng)絡(luò) 分享至：

(1) ASTM G34-23 Standard test method for exfoliation corrosion（剝落腐蝕） susceptibility in 2XXX and 7XXX series Aluminum alloys(EXCO test)

(2) ASTM G47-22 Standard Test Method for Determining Susceptibility to Stress Corrosion Cracking（應(yīng)力腐蝕開裂） of 2XXX and 7XXX Aluminum Alloy Products

(3) ASTM G66-23 Standard test method for visual assessment of exfoliation corrosion susceptibility of 5XXX series aluminum alloys(ASSET Test)

(4) ASTM G67-18 Standard test method for determining the susceptibility to intergranular corrosion（晶間腐蝕） of 5XXX series aluminum alloys by mass loss after exxposure to Nitric Acid(NAMLT Test)

(5) ASTM G69-20 Standard test method for measurement of corrosion potentials（腐蝕電位） of alluminum alloys

(6) ASTM G103-1997R23(e1) Standard practice for evaluating stress corrosion cracking resistance of low copper 7XXX series Al-Zn-Mg-Cu alloys in boiling 6% sodium chloride solution

(7) ASTM G110-92（2022）e2 Standrad practice for evaluating intergranular corrosion resistance of heat treable aluminum alloys by immersion in Sodium Chloride + Hydrogen Pereoxide solution

(8) ASTM G112-2022 Standard Gudie for conducting exfoliation corrosion tests in aluminum alloys

(9) ASTM G139-05（2022） Test Method for determining stress corrosion cracking resistance of heat-treable Aluminum Alloy products using Breaking Load method

(10) GB/T 7998-2005 鋁合金晶間腐蝕測定方法（Test method for intergranular corrosion of aluminum alloy),參考ASTM G110-1992

(11) GB/T 7998-2023 鋁合金晶間腐蝕敏感性評價方法（Method for evaluating the suscetibility to intergranular corrosion of alumunum alloys),替代GB/T 79998-2005he GB/T 26491-2011《5XXXX系鋁合金晶間腐蝕試驗方法質(zhì)量損失法》，適用于2、5、6、7系鋁合金產(chǎn)品晶間腐蝕敏感性的測定。

(12) GB/T 22640-2023 鋁合金應(yīng)力腐蝕敏感性評價試驗方法（Test method for determining susceptibility to stress corrosion cracking of aluminum alloys)

適用于：C型環(huán)試樣恒應(yīng)變、彎梁試樣恒應(yīng)變、U型試樣恒應(yīng)變、拉伸試樣恒載荷、拉伸試樣恒應(yīng)變、拉伸試樣慢速率拉伸、沸騰氯化鈉溶液恒應(yīng)變等；（2系-Cu1.8%~7.0%、6系、7系-Cu0.4%~2.8%）

(13) GB/T 26323-2010 色漆和清漆鋁及及合金表面涂膜的耐絲狀腐蝕試驗（Paints and varnishes - determination of resistance to filiform corrosion on aluminum and aluminum alloys( ISO 4623-2:2003 MOD)

(14) GB/T 33883-2017 7XXX系鋁合金應(yīng)力腐蝕沸騰氯化鈉溶液法（銅含量低于1.2%）

(15) GB/T 36174-2018 金屬和合金的腐蝕固溶熱處理鋁合金的耐晶間腐蝕性的測定（ ISO 11846:1995，IDT）

(16) GB/T 40388-2021 金屬和合金的腐蝕鋁合金剝落腐蝕試驗（ISO 11881:1999，MOD）

(17) GB/T 41653-2022 金屬和合金的腐蝕熱處理鋁合金晶間腐蝕敏感性陽極試驗方法（ corrosion of metals and alloys - anodic test for evaluation of intergranular corrosion susceptibility of heat treatable aluminum alloys）ISO 15329:2006，MOD

(18) GB/T 42514-2023 鋁及鋁合金陽極氧化膜及有機(jī)聚合物膜的腐蝕評定圖表法（ ISO 8993:2018，NEQ）

(19) GB/T 42544-2023 鋁及鋁合金陽極氧化膜及有機(jī)聚合物膜的腐蝕評定柵格法（ISO 8994:2018，NEQ）

(20) HB 5254-83 變形鋁合金拉伸應(yīng)力腐蝕試驗方法

(21) HB 5255-83 鋁合金晶間腐蝕及晶間腐蝕傾向的測定

(22) HB 5259-83 鋁合金C環(huán)試樣應(yīng)力腐蝕試驗方法

(23) HB 5294-84 高強(qiáng)度鋁合金雙懸臂（DCB）試樣應(yīng)力腐蝕試驗方法

(24) MH/T 6071-2011 夾層腐蝕試驗方法Test method for sandwich corrosion test

(25) SH/T 0620-95 發(fā)動機(jī)冷卻液對傳熱狀態(tài)下的鑄鋁合金腐蝕測定法（等效采用ASTM D4340）

(26) SJ 30046-2019 鋁合金晶間腐蝕試驗方法

(27) SJ 30047-2019 鋁合金剝落腐蝕試驗方法

(28) T/CCTAS 54-2023 軌道交通車輛用鋁合金材料晶間腐蝕測定方法

(29) T/CCTAS 55-2023 軌道交通車輛用抗應(yīng)力腐蝕鋁合金材料過程控制要求