NACE TM0177-2024 Laboratory Testing of Metals for resistance to Sulfide Stress Cracking and Stress Corrosion Cracking in H2S Environments 金屬在硫化氫環境中抗硫化物應力開裂和應力腐蝕開裂的實驗室試驗方法。2024最新版主要章節有：

• Foreword and Scope

• Rationale

• 1 General

• 2 Environmental Cracking Testing Variability

• 3 Reagents

  • 3.1 Reagent Purity

• 4 Test Specimens and Material Properties

• 5 Test Vessels and Fixtures

• 6 Test Solutions

  • 6.1 General

  • 6.2 Test Solution A

  • 6.3 Test Solution B

  • 6.4 Test Solution C

  • 6.5 Test Solution D

  • 6.7 Deaeration Requirements and Precedures

  • 6.8 Solution Test Gas Saturation Requirements

• 7 Test under Non-Ambient Conditions

  • 7.3 Approach

  • 7.4 Test Equipment

  • 7.5 Test Solution

  • 7.6 Test Gas

  • 7.7 Test Stresses

  • 7.8 Test Procedure

• 8 Method A——NACE Standard Tensile Test

• 9 Method B——NACE Standard Three-Point Bent-Beam Test

• 10 Method C——NACE Standard C-Ring Test

• 11 Method D——NACE Standard Double Cantilever Beam Test

• References

• Appendix A~G

NACE TM0177標準最早于1977年制定，并在1986年、1996年、2005年、2016年和2024年進行了修訂。